If you are a really old potter, like me, you will remember that message! Remember how it would come up occasionally when the TV transmission was bad? OK, maybe I'm the only one old enough....
But, if you are wondering why I haven't been posting, that is the reason. The video card in my computer packed up and left for Saturn, leaving me with a nice black (not blue, but still bad) screen. I was able to attach a smaller screen, bypassing the video card, but it has the wrong aspect ratio and everything on my screen is s-t-r-e-t-c-h-e-d, making all dogs look like Dachies, all pots look like short bowls....
I'll post again once I get a new video card (or a new computer).
The scary thing is, w-i-d-e letters are starting to look normal!
An occasional blog about pottery, making pots, and living the life of a potter.
Monday, October 28, 2013
Sunday, September 29, 2013
Shaw Woods Mugs
Spent a large part of last week decorating some mugs for the Shaw Woods. They are having an open day next Sunday, Oct. 6, with guided hikes, workshops, information and some fund-raising items. And some of those will be my mugs!
I worked hard at painting them, holding my (metaphorical) breath on the subject of DOTS.
My pots look so nice when they are painted and before they are fired! I almost don't want to fire them. Of course they look soft and 'dusty' and pale.... but full of hope.
Happily, sometimes they come out of the firing still looking good!
And no dots, whew.
P.S. You can get more info about the Shaw Woods, and register for one of the public hikes, at their website. If you are in the area (Ottawa), come out and enjoy a great day in a special place. And maybe you'll see my mugs there!
I worked hard at painting them, holding my (metaphorical) breath on the subject of DOTS.
My pots look so nice when they are painted and before they are fired! I almost don't want to fire them. Of course they look soft and 'dusty' and pale.... but full of hope.
Happily, sometimes they come out of the firing still looking good!
And no dots, whew.
P.S. You can get more info about the Shaw Woods, and register for one of the public hikes, at their website. If you are in the area (Ottawa), come out and enjoy a great day in a special place. And maybe you'll see my mugs there!
Sunday, September 15, 2013
Safety First
For those just thinking of setting up a pottery studio, or for anyone whose workplace could use a safety tune-up, I've put together a short list of aids to safety that you don't want to be without.
One of the biggest worries is, of course, fire. Make sure you have a good fire extinguisher:
Sometimes the power will go off, leaving you all alone is a pitch-black studio filled with tables, wheels, wet clay, sleeping dogs to trip over.... An emergency lighting system is a must.
Of course, if you can afford it, an auxiliary power supply is even better.
Industrial accidents are another big concern. As they say, accidents do happen. Make sure you are prepared.
And if all else fails, make sure you have what you need to call for help.
With a little foresight, you ought to be able to enjoy years of happy potting without disaster. All it takes is a little advance planning.
One of the biggest worries is, of course, fire. Make sure you have a good fire extinguisher:
Sometimes the power will go off, leaving you all alone is a pitch-black studio filled with tables, wheels, wet clay, sleeping dogs to trip over.... An emergency lighting system is a must.
Of course, if you can afford it, an auxiliary power supply is even better.
Industrial accidents are another big concern. As they say, accidents do happen. Make sure you are prepared.
And if all else fails, make sure you have what you need to call for help.
With a little foresight, you ought to be able to enjoy years of happy potting without disaster. All it takes is a little advance planning.
Friday, August 30, 2013
Butter Dishes
Made a nice batch of butter dishes. I glazed them in solid colours, except for the 'Bird' design ones - some pale green, some yellow, some turquoise, some medium blue, some deep indigo blue. I played with the handles and made strap handles, bird handles, loopy handles.... striped and dotted ones. Lots of fun!
Taking the photo to show one of them on my Facebook page (Pine Ridge Studio is on Facebook) was difficult. I just couldn't get it to look like much. Luckily my friend Janice happened by with a lovely gift of ripe tomatoes from her garden and I grabbed her. Her painter's eye quickly zeroed in on using the darker areas of the image to create a dynamic composition.
Notice the neat triangle made by the bird, the dark vase, and the butter knife. Thank you, Janice!
Now, just don't ask me why flowers because I don't know. I just thought they would look fresh with the butter and I think of breakfast, which is when I like butter on my toast, as a fresh time of day.
And no dots, you'll notice.
Taking the photo to show one of them on my Facebook page (Pine Ridge Studio is on Facebook) was difficult. I just couldn't get it to look like much. Luckily my friend Janice happened by with a lovely gift of ripe tomatoes from her garden and I grabbed her. Her painter's eye quickly zeroed in on using the darker areas of the image to create a dynamic composition.
Notice the neat triangle made by the bird, the dark vase, and the butter knife. Thank you, Janice!
Now, just don't ask me why flowers because I don't know. I just thought they would look fresh with the butter and I think of breakfast, which is when I like butter on my toast, as a fresh time of day.
And no dots, you'll notice.
Sunday, August 4, 2013
Dots, grrrrrrr.....
Well, it's back to square one, folks.
A longer, slower bisque firing had no effect. I didn't think it would. How can stuff that is supposed to burn out at cone 06 affect things at cone 6? Unless my brain is slipping a gear, I can't see the connection. Anyway, it didn't make any difference. Dots and more dots....
Unless it is something really subtle about the firing (the glaze firing, that is), I guess it is the clay. Maybe the first batch of the clay I got to test - remember, I switched clay bodies to try to get away from the problem of teapots cracking after a year or two of use - was not the same as this clay now. Every batch is a wee bit different, I am thinking. I am sure there was no problem with dots when I decided to make the switch. I would have noticed at once.
So now I am trying two things: a bunch of things thrown using the old clay and glazed in the current batch of glaze, and some in the new clay using slightly different versions of the glaze. Maybe a version with slightly more frit will melt a bit more and the dots either won't form or will heal over at temperature. Or a version with slightly less opacifier might not form dots. I tested both of those ideas a week ago and got no dots on either, but I didn't think it likely both ideas would have worked, so decided to discount those tests. Maybe I was too quick about that.
Come to think of it, I should try a small batch of this glaze with no opacifier and see if it gets dots. I'll go do that right now, a glaze firing is coming up in the next day or two so I'll go and get it ready. Put it on both clays and see what happens.
One thing that makes this problem frustrating is the lack of information on it. Every reference to 'dots' that I have found so far just says that they are a known issue in maiolica work, but suggestions on how to fix the problem are scarce. Basically, 'use a different glaze' and 'use a different clay' and 'use a different technique' and 'just accept it' are about it for suggestions..... like I said, square one.
A longer, slower bisque firing had no effect. I didn't think it would. How can stuff that is supposed to burn out at cone 06 affect things at cone 6? Unless my brain is slipping a gear, I can't see the connection. Anyway, it didn't make any difference. Dots and more dots....
Unless it is something really subtle about the firing (the glaze firing, that is), I guess it is the clay. Maybe the first batch of the clay I got to test - remember, I switched clay bodies to try to get away from the problem of teapots cracking after a year or two of use - was not the same as this clay now. Every batch is a wee bit different, I am thinking. I am sure there was no problem with dots when I decided to make the switch. I would have noticed at once.
So now I am trying two things: a bunch of things thrown using the old clay and glazed in the current batch of glaze, and some in the new clay using slightly different versions of the glaze. Maybe a version with slightly more frit will melt a bit more and the dots either won't form or will heal over at temperature. Or a version with slightly less opacifier might not form dots. I tested both of those ideas a week ago and got no dots on either, but I didn't think it likely both ideas would have worked, so decided to discount those tests. Maybe I was too quick about that.
Come to think of it, I should try a small batch of this glaze with no opacifier and see if it gets dots. I'll go do that right now, a glaze firing is coming up in the next day or two so I'll go and get it ready. Put it on both clays and see what happens.
One thing that makes this problem frustrating is the lack of information on it. Every reference to 'dots' that I have found so far just says that they are a known issue in maiolica work, but suggestions on how to fix the problem are scarce. Basically, 'use a different glaze' and 'use a different clay' and 'use a different technique' and 'just accept it' are about it for suggestions..... like I said, square one.
Sunday, July 21, 2013
Dots.... Onwards in the Quest
Well, I'm still working on the dots problem. For a day or two I actually thought that it might be due to over-firing as the shelf with the worst case of the dots was definitely over-fired, but then reality set in.
I fired another load of maiolica-type work and made sure to have witness cones on every shelf. This confirmed that the bottom of the kiln was over-firing. I debated switching the top and bottom thermocouples but in the end didn't and just went back to my old system of having a deep space on the bottom and shallower spaces higher up the kiln, and placing a kiln shelf right at the top. I also went back to leaving the top peep hole open. Don't ask me why this works, but for me it does. Maybe my kiln vent is just weird, but it worked before with the manual kiln and is working again now with this computer-controlled one. The original thermocouples gave a very even firing, but this second set clearly doesn't. So I at least learned that much. The firing was much more even.
But dots appeared on every shelf.
Then I sent an SOS out on Clayart, a list I belong to. This list (if you aren't on it, you should be) has some super helpful and knowledgeable people on it, and I got a number of responses. Some of the suggestions made were: could be the opacifier; fire the bisque higher or longer to be sure it is well cleared; re-screen the glaze; could be the clay; could be a change in glaze material; try another glaze; fire slower.
I tried re-screening the glaze first. Easiest thing to check! This had no real effect except that I did realize that the thickness of the glaze slurry had drifted and it needed more dilution. I mix large batches of this white glaze, keep it in a laundry tub for dipping large pieces, and just add to it whenever the level goes down too far. That doesn't mean it doesn't get screened except when being mixed, though. I periodically re-screen the whole batch. The frit (F3134) is somewhat soluble, and I think it gets used up differentially. So I sometimes add a titch of frit and that means re-screening and testing. Plus the glaze sometimes develops tiny granules. They dissolve when I touch them, but I figure they can't be good so when I see more than one or two on a glazed piece, I re-screen. But in fact this glaze had been standing more than usual lately, because I have been making stuff in a couple of plain colours in order to have lower-priced pieces to sell. So it made sense to try that first.
Unfortunately, as I said, that had no effect.
I couldn't really try a different opacifier. I have been using Superpax and it is not a new bag. Tin Oxide has lots of problems, not the least of which is that it is expensive. So I don't want to get into that. Plus the small amount I have has crystallized badly....
I tried a slower, slightly higher bisque. This had no noticeable effect either. One problem I have, my Studio is in a rural area, and our electric current fluctuates. We are supposed to have 'time of use' pricing, that is, hydro is supposed to be cheaper during the off-peak hours. I have tried firing at night, but have found that the firings take longer so I'm not sure I'm ahead at all. I've tried to talk to my hydro supplier, but they don't talk to humans. Long story short, my bisque firings, all on the 'slow bisque' program my kiln has, vary between 8.5 and 14 hours. That's not particularly fast. Still, I tried a cone 05 firing to see if it made a difference, but it didn't seem to.
None of my glaze materials are new, and none are particularly old, or have gotten damp or frozen or any other such thing.
Yes, I have changed clay. But I changed clay months ago, and for three months there were no dots. No pinholes, no bubbles, no dots.
I really don't want to change to a completely new glaze. I could try my clear glaze with opacifier, but it doesn't take the colours nearly as well as my white one does.
And fire slower? How can I when the current fluctuates so much? I can program to my heart's content, but if the elements don't get the power they need, they are going to slow down. Glaze firings also vary a lot, everywhere from 6.8 hours to 12.6. I log every firing, so I know.
So what to do? Well, I tried two things in the latest load: a batch of glaze with 3% more frit 3134, and a batch with 2% less Superpax. I dipped a mug, new clay, slow-bisqued to cone 06, in each, plus one in the large glaze batch in the tub.
Here is the result. They were all on the same shelf in a well-loaded but not tight, kiln. The witness cone is nicely bent over, tip touching the little plate I put it on. The firing to cone 6 took 8.51 hours.
The left-hand mug, with the tomatoes, is the glaze in the large tub. The middle one, with the peas showing, is the low Superpax version (it is slightly less white), and the carrots are the higher frit version.
NO DOTS!
Boy, am I confused now.
Well, guess I'll go drive the garbage out to the road for tomorrow's collection - they come so darn early I have to do it the night before and hope the critters don't get into it, ravens or racoons or skunks or the neighbour's dog - and let my subconscious work on the problem overnight.
I fired another load of maiolica-type work and made sure to have witness cones on every shelf. This confirmed that the bottom of the kiln was over-firing. I debated switching the top and bottom thermocouples but in the end didn't and just went back to my old system of having a deep space on the bottom and shallower spaces higher up the kiln, and placing a kiln shelf right at the top. I also went back to leaving the top peep hole open. Don't ask me why this works, but for me it does. Maybe my kiln vent is just weird, but it worked before with the manual kiln and is working again now with this computer-controlled one. The original thermocouples gave a very even firing, but this second set clearly doesn't. So I at least learned that much. The firing was much more even.
But dots appeared on every shelf.
Then I sent an SOS out on Clayart, a list I belong to. This list (if you aren't on it, you should be) has some super helpful and knowledgeable people on it, and I got a number of responses. Some of the suggestions made were: could be the opacifier; fire the bisque higher or longer to be sure it is well cleared; re-screen the glaze; could be the clay; could be a change in glaze material; try another glaze; fire slower.
I tried re-screening the glaze first. Easiest thing to check! This had no real effect except that I did realize that the thickness of the glaze slurry had drifted and it needed more dilution. I mix large batches of this white glaze, keep it in a laundry tub for dipping large pieces, and just add to it whenever the level goes down too far. That doesn't mean it doesn't get screened except when being mixed, though. I periodically re-screen the whole batch. The frit (F3134) is somewhat soluble, and I think it gets used up differentially. So I sometimes add a titch of frit and that means re-screening and testing. Plus the glaze sometimes develops tiny granules. They dissolve when I touch them, but I figure they can't be good so when I see more than one or two on a glazed piece, I re-screen. But in fact this glaze had been standing more than usual lately, because I have been making stuff in a couple of plain colours in order to have lower-priced pieces to sell. So it made sense to try that first.
Unfortunately, as I said, that had no effect.
I couldn't really try a different opacifier. I have been using Superpax and it is not a new bag. Tin Oxide has lots of problems, not the least of which is that it is expensive. So I don't want to get into that. Plus the small amount I have has crystallized badly....
I tried a slower, slightly higher bisque. This had no noticeable effect either. One problem I have, my Studio is in a rural area, and our electric current fluctuates. We are supposed to have 'time of use' pricing, that is, hydro is supposed to be cheaper during the off-peak hours. I have tried firing at night, but have found that the firings take longer so I'm not sure I'm ahead at all. I've tried to talk to my hydro supplier, but they don't talk to humans. Long story short, my bisque firings, all on the 'slow bisque' program my kiln has, vary between 8.5 and 14 hours. That's not particularly fast. Still, I tried a cone 05 firing to see if it made a difference, but it didn't seem to.
None of my glaze materials are new, and none are particularly old, or have gotten damp or frozen or any other such thing.
Yes, I have changed clay. But I changed clay months ago, and for three months there were no dots. No pinholes, no bubbles, no dots.
I really don't want to change to a completely new glaze. I could try my clear glaze with opacifier, but it doesn't take the colours nearly as well as my white one does.
And fire slower? How can I when the current fluctuates so much? I can program to my heart's content, but if the elements don't get the power they need, they are going to slow down. Glaze firings also vary a lot, everywhere from 6.8 hours to 12.6. I log every firing, so I know.
So what to do? Well, I tried two things in the latest load: a batch of glaze with 3% more frit 3134, and a batch with 2% less Superpax. I dipped a mug, new clay, slow-bisqued to cone 06, in each, plus one in the large glaze batch in the tub.
Here is the result. They were all on the same shelf in a well-loaded but not tight, kiln. The witness cone is nicely bent over, tip touching the little plate I put it on. The firing to cone 6 took 8.51 hours.
The left-hand mug, with the tomatoes, is the glaze in the large tub. The middle one, with the peas showing, is the low Superpax version (it is slightly less white), and the carrots are the higher frit version.
NO DOTS!
Boy, am I confused now.
Well, guess I'll go drive the garbage out to the road for tomorrow's collection - they come so darn early I have to do it the night before and hope the critters don't get into it, ravens or racoons or skunks or the neighbour's dog - and let my subconscious work on the problem overnight.
Friday, June 14, 2013
Dotty Update
One thing about pottery, it is not quick. Just figuring out what happened to cause all those 'dots' I talked about last post took me a week, and I was lucky it was only one week. I found the problem right away.
I re-fired several of the mugs, each on a different shelf in the kiln. I made sure to have large witness cones near each one.
Bingo.
The bottom shelf was almost a full cone over-fired. The witness cone for Cone 7 was fully over. The other shelves were the Cone 6 as I expected.
So I'm figuring the problem is the thermo-couple at the bottom of the kiln. This problem of 'dots' has been creeping up on a me a bit so I guess the thermo-couple has been failing gradually. I just didn't twig to the fact that it was always the pieces on the bottom that were acquiring a 'dotty' nature in the firing.
Well. Lesson learned. From now on I will put in witness cones at least every 3rd or 4th firing. I've been slack about that. They tell you to use them every firing, but with a computer-controlled kiln it is hard to convince yourself to actually do it. Especially in really full loads.... and especially when you stop to think of how much those darn things cost.
Re-firing didn't affect the dots, by the way. They neither got worse nor got better. And I even tried applying dabs of colour to the dots and re-firing and that didn't work because I couldn't get enough on to really cover the white.
Another learning experience.... if I learn from my mistakes, I'm going to be awful smart some day.
I re-fired several of the mugs, each on a different shelf in the kiln. I made sure to have large witness cones near each one.
Bingo.
The bottom shelf was almost a full cone over-fired. The witness cone for Cone 7 was fully over. The other shelves were the Cone 6 as I expected.
So I'm figuring the problem is the thermo-couple at the bottom of the kiln. This problem of 'dots' has been creeping up on a me a bit so I guess the thermo-couple has been failing gradually. I just didn't twig to the fact that it was always the pieces on the bottom that were acquiring a 'dotty' nature in the firing.
Well. Lesson learned. From now on I will put in witness cones at least every 3rd or 4th firing. I've been slack about that. They tell you to use them every firing, but with a computer-controlled kiln it is hard to convince yourself to actually do it. Especially in really full loads.... and especially when you stop to think of how much those darn things cost.
Re-firing didn't affect the dots, by the way. They neither got worse nor got better. And I even tried applying dabs of colour to the dots and re-firing and that didn't work because I couldn't get enough on to really cover the white.
Another learning experience.... if I learn from my mistakes, I'm going to be awful smart some day.